The purpose of this paper is to investigate the feasibility of using land grid array (LGA) solder joints as a second-level interconnection option in low-temperature co-fired ceramic (LTCC)/printed wiring board (PWB) assemblies for telecommunication applications. The characteristic behaviour of two commercial lead-free solder materials (Sn4Ag0.5Cu and Sn3Ag0.5Cu0.5In0.05Ni) in reflow processes and thermal cycling tests are also evaluated.

The effect of the reflow temperature profile on voiding in two lead-free solders in LTCC/PWB assemblies was investigated using X-ray and scanning electron microscopy (SEM) investigations. The test assemblies were fabricated and exposed to a temperature cycling test (TCT) in a 0-100°C or −40 to 125°C temperature range. Organic PWB material with a low coefficient of thermal expansion (CTE) was primarily used. In addition, to compare LGA assemblies with low and high global thermal mismatches, an LTCC module/FR-4 assembly was also fabricated and exposed to a TCT in a 0-100°C temperature range. The characteristic lifetime of the test assemblies was determined using DC resistance measurements. The failure mechanisms of the interconnections were verified using scanning acoustic microscopy, SEM and finite element (FE)-SEM investigations.

This work showed that the solderability of AgPt-metallized LTCC modules was poor, resulting in excessive voiding. This problem was avoided by using pre-tinned modules. In the test assemblies, the Sn4Ag0.5Cu joints had a lower void content and a higher characteristic lifetime compared with the Sn3Ag0.5Cu0.5In0.05Ni joints. Furthermore, it was observed that the Sn3Ag0.5Cu0.5In0.05Ni joints were more prone to fail along the interface between the Ag₃Sn layer and the solder matrix than were the Sn4Ag0.5Cu joints. It was assumed that the observed difference in the primary failure mechanisms resulted in the decreased lifetime duration of the SnAgCu-InNi/Arlon in both temperature cycling conditions.

The results proved that the solderability of both solders in AgPt-metallized modules in a typical surface mount technology process was poor; however, the solderability of the test modules can be notably enhanced with pre-tinned pads. This work also demonstrated the effect of the metallization/solder pair on the failure mechanisms and failure rate in LTCC/PWB assemblies with LGA joints; the work also proved in the TCT, over a temperature range of 0-100°C, that using the present LGA joints in LTCC/PWB assemblies with a high global thermal mismatch did not increase the lifetime duration of the joints to the preferred level (3,000 cycles), whereas the performance of these joints was adequate in assemblies with a low global thermal mismatch. Moreover, the results indicated that using the LGA joint configuration enhanced the reliability of the LTCC/PWB assemblies compared with similar assemblies with collapsible ball grid array solder spheres.

To investigate the effect of the metallization and solder mask materials on the solder joint reliability of low temperature co‐fired ceramic (LTCC) modules.

The fatigue performance of six LTCC/PCB assembly versions was investigated using temperature cycling tests in the −40‐125°C and 20‐80°C temperature ranges. In order to eliminate fatigue cracking in the LTCC module itself, large AgPt‐metallized solder (1 mm) lands with organic or co‐fired glaze solder masks, having 0.86‐0.89 mm openings, were used. The performance of these modules was compared to that of AgPd‐metallized modules with a similar solder land structure. The joint structures were analysed using resistance measurements, scanning acoustic microscopy, SEM/EDS investigation, and FEM simulations.

The results showed that failure distributions with Weibull shape factor (β) values from 8.4 to 14.2, and characteristic life time (θ) values between 860 and 1,165 cycles were achieved in AgPt assemblies in the −40‐125°C temperature range. The primary failure mechanism was solder joint cracking, whereas the AgPd‐metallized modules suffered from cracking in the ceramic. In the milder test conditions AgPd‐metallized modules showed better fatigue endurance than AgPt‐metallized modules.

This paper proves that the cracking in ceramic in the harsh test condition can be eliminated almost completely by using AgPt metallization instead of AgPd metallization in the present test module structure.

This paper aims to investigate the metallurgical reactions between two commercial AgPt thick films used as a solder land on a low temperature co‐fired ceramic (LTCC) module and solder materials (SnAgCu, SnInAgCu, and SnPbAg) in typical reflow conditions and to clarify the effect of excessive intermetallic compound (IMC) formation on the reliability of LTCC/printed wiring boards (PWB) assemblies.

Metallurgical reactions between liquid solders and AgPt metallizations of LTCC modules were investigated by increasing the number of reflow cycles with different peak temperatures. The microstructures of AgPt metallization/solder interfaces were analyzed using SEM/EDS investigation. In addition, a test LTCC module/PWB assembly with an excess IMC layer within the joints was fabricated and exposed to a temperature cycling test in a −40 to 125°C temperature range. The characteristic lifetime of the test assembly was determined using DC resistance measurements. The failure mechanism of the test assembly was verified using scanning acoustic microscopy and SEM investigation.

The results showed that the higher peak reflow temperature of common lead‐free solders had a significant effect on the consumption of the original AgPt metallization of LTCC modules. The results also suggested that the excess porosity of the metallization accelerated the degradation of the metallization layer. Finally, the impact of these adverse metallurgical effects on the actual failure mechanism in an LTCC/PWB assembly was demonstrated.

This paper proves how essential it is to know the actual LTCC metallization/solder interactions that occur during reflow soldering and to recognize their effect on solder joint reliability in LTCC module/PWB assemblies. Moreover, the adverse effect of using lead‐free solders on the degradation of Ag‐based metallizations and, consequently, on board level reliability is demonstrated. Finally, practical guidelines for selecting materials for second‐level solder interconnections of LTCC module are given.